| Product Description |
|
Ultramid B3WG6 CR BK23210 s a 30% glass fiber reinforced, heat stabilized injection molding PA6 grade for crash relevant
applications. |
| PHYSICAL |
ISO Test Method |
Property Value |
| Density, g/cm³ |
1183 |
1.36 |
| Moisture, % |
62 |
|
| (50% RH) |
|
2.1 |
| (Saturation) |
|
6.6 |
| RHEOLOGICAL |
ISO Test Method |
Dry |
Conditioned |
| Melt Volume Rate (275 °C/5 Kg), cc/10min. |
1133 |
30 |
- |
| MECHANICAL |
ISO Test Method |
Dry |
Conditioned |
| Tensile Modulus, MPa |
527 |
|
|
| 23°C |
|
9,500 |
5,600 |
| Tensile stress at break, MPa |
527 |
|
|
| 23°C |
|
170 |
100 |
| Tensile strain at break, % |
527 |
|
|
| 23°C |
|
3.4 |
7.5 |
| IMPACT |
ISO Test Method |
Dry |
Conditioned |
| Charpy Notched, kJ/m² |
179 |
|
|
| 23°C |
|
12.5 |
- |
| -30°C |
|
8.5 |
- |
| Charpy Unnotched, kJ/m² |
179 |
|
|
| 23°C |
|
95 |
105 |
| THERMAL |
ISO Test Method |
Dry |
Conditioned |
| Melting Point, °C |
3146 |
220 |
- |
| HDT A, ° C |
75 |
205 |
- |
| Note |
|
Although all statements and information in this publication are believed to be accurate and reliable, they are presented gratis and for guidance only, and risks and liability for results obtained by use of the products or application of the suggestions described are assumed by the user. NO WARRANTIES OF ANY KIND, EITHER EXPRESS OR IMPLIED, INCLUDING WARRANTIES OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE, ARE MADE REGARDING PRODUCTS DESCRIBED OR DESIGNS, DATA OR INFORMATION SET FORTH. Statements or suggestions concerning possible use of the products are made without representation or warranty that any such use is free of patent infringement and are not recommendations to infringe any patent. The user should not assume that toxicity data and safety measures are indicated or that other measures may not be required. |
|
|