| Product Description |
|
Nypel RC6024 BK is a black pigmented, semi crystalline, heat stabilized,
low viscosity, 30% mineral and glass fiber reinforced injection molding
compound based on recycled PA6 feedstocks. It possesses a balance of
engineering properties in combination with excellent dimensional stability,
good flow and processability, low warp and good chemical, abrasion and
sink-mark formation resistance.
|
| Applications |
|
Nypel RC6024 BK is generally recommended for applications such as
rotors, wheels, rims, timing belt covers, automotive cooling fans
and shrouds.
|
| PHYSICAL |
ISO Test Method |
Property Value |
| Density, g/cm³ |
1183 |
1.38 |
| MECHANICAL |
ISO Test Method |
Dry |
Conditioned |
| Tensile Modulus, MPa |
527 |
|
|
| 23°C |
|
600 |
- |
| Tensile stress at break, MPa |
527 |
|
|
| 23°C |
|
100 |
- |
| Tensile strain at break, % |
527 |
|
|
| 23°C |
|
3.6 |
- |
| Flexural Modulus, MPa |
178 |
|
|
| 23°C |
|
5,960 |
- |
| IMPACT |
ISO Test Method |
Dry |
Conditioned |
| Izod Notched Impact, kJ/m² |
180 |
|
|
| 23°C |
|
4.2 |
- |
| -40°C |
|
4.6 |
- |
| Charpy Notched, kJ/m² |
179 |
|
|
| 23°C |
|
3.5 |
- |
| THERMAL |
ISO Test Method |
Dry |
Conditioned |
| HDT A, ° C |
75 |
180 |
- |
| Note |
|
Although all statements and information in this publication are believed to be accurate and reliable, they are presented gratis and for guidance only, and risks and liability for results obtained by use of the products or application of the suggestions described are assumed by the user. NO WARRANTIES OF ANY KIND, EITHER EXPRESS OR IMPLIED, INCLUDING WARRANTIES OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE, ARE MADE REGARDING PRODUCTS DESCRIBED OR DESIGNS, DATA OR INFORMATION SET FORTH. Statements or suggestions concerning possible use of the products are made without representation or warranty that any such use is free of patent infringement and are not recommendations to infringe any patent. The user should not assume that toxicity data and safety measures are indicated or that other measures may not be required. |
|
|