| Product Description |
|
Luran S 797 SE is an extrusion ASA grade with especially high notched impact
strength, used for sheet and profile extrusions. The data representable is based
on extruded sheet. |
| RHEOLOGICAL |
ASTM Test Method |
Property Value |
| Melt Volume Rate 220 °C/10 Kg |
D-1238 |
5 |
| PHYSICAL |
ASTM Test Method |
Property Value |
| Specific Gravity |
D-792 |
1.07 |
| Mold Shrink, Linear-Flow (in/in) |
D-955 |
0.0055 |
| Water absorption saturated at 23°C, % |
D-570 |
1.65 |
| MECHANICAL |
ASTM Test Method |
Property Value |
| Rockwell Hardness, R Scale |
D-785 |
90 |
| Tensile Modulus, MPa (psi) |
D-638 |
|
| 23°C (73°F) |
|
1,830 (265,000) |
| Tensile Strength, Yield (2in/min), MPa (psi) |
D-638 |
|
| 23°C (73°F) |
|
40 (5,800) |
| Elongation, Yield (2in/min), % |
D-638 |
|
| 23°C (73°F) |
|
2.9 |
| Flexural Modulus, MPa (psi) |
D-790 |
|
| 23°C (73°F) |
|
1,560 (226,000) |
| Flexural Strength, MPa (psi) |
D-790 |
|
| 23°C (73°F) |
|
57 (8,270) |
| IMPACT |
ASTM Test Method |
Property Value |
| Notched Izod Impact, J/M (ft-lbs/in) |
D-256 |
|
| -40°C (-40°F) |
|
57 (1.1) |
| 23°C (73°F) |
|
280 (5.2) |
| THERMAL |
ASTM Test Method |
Property Value |
| DTUL @ 264 psi - Annealed °C(°F) |
D-648 |
82 (179) |
| Vicat, A/2 (50 deg. C/h, 50N), °C(°F) |
D-1525 |
90 (194) |
| ELECTRICAL |
ASTM Test Method |
Property Value |
| Volume Resistivity |
D-257 |
>1E12 |
| Surface Resistivity |
D-257 |
>1E13 |
| Dielectric Constant (1000000 Hz, 0,0394 in) |
D-150 |
3.3 |
| OPTICAL |
ASTM Test Method |
Property Value |
| Gloss, 60 °C, % |
D-523 |
91 |
| INJECTION PROCESSING |
|
Property Value |
| Drying Temperature, °C(°F) |
|
79 (174) |
| Drying Time, hr |
|
2 to 4 |
| Suggested Max. Regrind, % |
|
30 |
| Note |
|
Although all statements and information in this publication are believed to be accurate and reliable, they are presented gratis and for guidance only, and risks and liability for results obtained by use of the products or application of the suggestions described are assumed by the user. NO WARRANTIES OF ANY KIND, EITHER EXPRESS OR IMPLIED, INCLUDING WARRANTIES OF MERCHANTABILITY OR FITNESS FOR A PARTICULAR PURPOSE, ARE MADE REGARDING PRODUCTS DESCRIBED OR DESIGNS, DATA OR INFORMATION SET FORTH. Statements or suggestions concerning possible use of the products are made without representation or warranty that any such use is free of patent infringement and are not recommendations to infringe any patent. The user should not assume that toxicity data and safety measures are indicated or that other measures may not be required. |
|
|